密度 | 1.04g/cm3 | 熔體流動速率 | 2.5g/10min | 吸水率 | 0.3% |
規(guī)格級別 | 電鍍 | 缺口沖擊強(qiáng)度 | 23 | 成型收縮率 | 0.45% |
加工級別 | 吹塑級 |
|
產(chǎn)品簡述
密度 | 1.04g/cm3 | 熔體流動速率 | 2.5g/10min | 吸水率 | 0.3% |
規(guī)格級別 | 電鍍 | 缺口沖擊強(qiáng)度 | 23 | 成型收縮率 | 0.45% |
加工級別 | 吹塑級 |
詳細(xì)數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
物理性能 | 比重 | ASTM D-792 | 1.04 | ||
成型收縮率 | ASTM D-955 | 0.3-0.6 | % | ||
吸水率 | ASTM D-570 | 0.3 | % | ||
機(jī)械性能 | 伸長率 | ASTM D-638 | 11 | % | |
拉伸強(qiáng)度 | ASTM D-638 | 480 | kg/cm2 | ||
沖擊強(qiáng)度 | (Notched)1/8" | ASTM D-256 | 23 | kg.cm/cm | |
洛氏硬度 | ASTM D-785 | R-102 | R-Scale | ||
彎曲模量 | ASTM D-790 | 23000 | kg/cm2 | ||
彎曲強(qiáng)度 | ASTM D-790 | 630 | kg/cm2 | ||
流動系數(shù) | 200℃/5kg | ASTM D-1238 | 2.5 | G/10min | |
熱性能 | 熱變形溫度 | (Unannealed) | ASTM D-648 | 86 | ℃ |
軟化點 | ASTM D-1525-82 | 102 | ℃ | ||
燃燒率 | CSA-0.6 | HB | |||
燃燒率 | UL-94 | HB |