密度 | 1.06g/cm3 | 熔體流動速率 | 7g/10min | 吸水率 | 0.55% |
規(guī)格級別 | 擠出 | 缺口沖擊強度 | 320 | 成型收縮率 | 0.6% |
加工級別 | 擠出級,注塑級,脫模級 | 特性級別 | 耐磨,耐水解,高流動,耐候 |
|
產品簡述
密度 | 1.06g/cm3 | 熔體流動速率 | 7g/10min | 吸水率 | 0.55% |
規(guī)格級別 | 擠出 | 缺口沖擊強度 | 320 | 成型收縮率 | 0.6% |
加工級別 | 擠出級,注塑級,脫模級 | 特性級別 | 耐磨,耐水解,高流動,耐候 |
詳細數據
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數據 | 數據單位 | |
基本性能 | 熔體流動速率 | 220℃/10.0kg | ASTM D-1238 | 7.0 | g/10min |
熔體流動速率 | 260℃/5.0kg | ASTM D-1238 | 13 | g/10min | |
吸水率 | Equilibrium,23℃ | ASTM D-570 | 0.55 | % | |
物理性能 | 比重 | ASTM D-792 | 1.06 | g/cm3 | |
模具收縮率 | Flow,3.20mm | ASTM D-955 | 0.50-0.70 | % | |
機械性能 | 拉伸模量 | ASTM D-638 | 1790 | MPa | |
拉伸屈服強度 | ASTM D-638 | 41.4 | MPa | ||
拉伸斷裂強度 | ASTM D-638 | 34.5 | MPa | ||
拉伸斷裂伸長率 | ASTM D-638 | 40 | % | ||
彎曲模量 | 50.0mm Span | ASTM D-790 | 1790 | MPa | |
彎曲屈服強度 | 50.0mm Span | ASTM D-790 | 58.6 | MPa | |
IZOD缺口沖擊強度 | -30℃ | ASTM D-256 | 58.7 | J/m | |
IZOD缺口沖擊強度 | 23℃ | ASTM D-256 | 320 | J/m | |
洛氏硬度 | ASTM D-785 | 86 | R scale | ||
電氣性能 | 表面電阻率 | ASTM D-257 | >1.0E+15 | ohms | |
介電強度 | 3.20mm,in Oil | ASTM D-149 | 16.0 | KV/mm | |
介電常數 | 50Hz | ASTM D-150 | 5.200 | ||
介電常數 | 60Hz | ASTM D-150 | 5.200 | ||
介電常數 | 1E+6Hz | ASTM D-150 | 3.210 | ||
介電損耗因數 | 50Hz | ASTM D-150 | 0.15 | ||
介電損耗因數 | 60Hz | ASTM D-150 | 0.15 | ||
介電損耗因數 | 1E+6Hz | ASTM D-150 | 0.26 | ||
熱性能 | 熱變形溫度 | 0.45MPa,未退火,3.20mm | ASTM D-648 | 87.8 | ℃ |
熱變形溫度 | 0.45MPa,未退火,6.40mm | ASTM D-648 | 90.6 | ℃ | |
熱變形溫度 | 1.80MPa,未退火,3.20mm | ASTM D-648 | 76.7 | ℃ | |
熱變形溫度 | 1.80MPa,未退火,6.40mm | ASTM D-648 | 79.4 | ℃ | |
熱變形溫度 | 1.80MPa,退火 | ASTM D-648 | 95.6 | ℃ | |
維卡軟化溫度 | ASTM D-1525 | 99.4 | ℃ | ||
CLTE | Flow,-30 TO 0℃ | ASTM E-831 | 0.000085 | cm/cm/℃ | |
CLTE | Flow,-40TO40℃ | ASTM E-831 | 0.000086 | cm/cm/℃ | |
CLTE | Flow,0TO100℃ | ASTM E-831 | 0.000090 | cm/cm/℃ | |
CLTE | Transverse,-40TO40℃ | ASTM E-831 | 0.000092 | cm/cm/℃ | |
燃燒性 | 1.50mm | UL 94 | HB | ||
RTI Str | UL 746 | 50.0 | ℃ | ||
RTI Imp | UL 746 | 50.0 | ℃ | ||
RTI Elec | UL 746 | 50.0 | ℃ |