密度 | 1.04g/cm3 | 熔體流動速率 | 4g/10min | 吸水率 | 0.04% |
缺口沖擊強度 | 196 | 成型收縮率 | 0.55% |
|
產(chǎn)品簡述
密度 | 1.04g/cm3 | 熔體流動速率 | 4g/10min | 吸水率 | 0.04% |
缺口沖擊強度 | 196 | 成型收縮率 | 0.55% |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
基本性能 | 熔體流動速率 | 200℃,5kg | ASTM D-1238 | 4.0 | g/10min |
吸水率 | 24hr | ASTM D-570 | 0.04 | % | |
物理性能 | 比重 | ASTM D-792 | 1.04 | g/cm3 | |
模具收縮率 | Flow | ASTM D-955 | 0.40-0.70 | % | |
機械性能 | 拉伸強度 | ASTM D-638 | 29.4 | MPa | |
拉伸斷裂伸長率 | ASTM D-638 | 50 | % | ||
彎曲模量 | ASTM D-790 | 1960 | MPa | ||
彎曲強度 | ASTM D-790 | 49.0 | MPa | ||
IZOD缺口沖擊強度 | ASTM D-256 | 196 | J/m | ||
洛氏硬度 | ASTM D-785 | 70 | L scale | ||
電氣性能 | 體積電阻率 | ASTM D-257 | 1.0E+17 | ohm.cm | |
介電常數(shù) | 1E+6Hz | ASTM D-150 | 2.500 | ||
熱性能 | 熱變形溫度 | 1.80MPa,未退火,6.40mm | ASTM D-648 | 76.0 | ℃ |
維卡軟化點 | Loading 1(10N) | ASTM D-1525 | 97.0 | ℃ | |
維卡軟化點 | Loading 2(50N) | ASTM D-1525 | 90.0 | ℃ | |
燃燒性 | 1.59mm,ALL | UL 94 | HB | ||
燃燒性 | 3.17mm,ALL | UL 94 | HB |