斷裂伸長率 | 900% | 拉伸強度 | 30MPa | 密度 | 0.963g/cm3 |
熔體流動速率 | 0.73g/10min | 加工級別 | 注塑級 | 特性級別 | 耐高溫 |
|
產(chǎn)品簡述
斷裂伸長率 | 900% | 拉伸強度 | 30MPa | 密度 | 0.963g/cm3 |
熔體流動速率 | 0.73g/10min | 加工級別 | 注塑級 | 特性級別 | 耐高溫 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 熔體流動速率 | ASTM D-1238 | 0.73 | g/10min | ||
密度 | ASTM D-4883 | 0.963 | g/cm3 | |||
屈服拉伸強度 | MD | ASTM D-882 | 39 | MPa | ||
TD | ASTM D-882 | 35 | MPa | |||
機械性能 | 斷裂拉伸強度 | MD | ASTM D-882 | 37 | MPa | |
TD | ASTM D-882 | 30 | MPa | |||
屈服伸長率 | MD | ASTM D-882 | 9 | % | ||
TD | ASTM D-882 | 9 | % | |||
斷裂伸長率 | MD | ASTM D-882 | 900 | % | ||
TD | ASTM D-882 | 900 | % | |||
1%正割模量 | MD | ASTM D-882 | 1030 | MPa | ||
TD | ASTM D-882 | 1100 | MPa | |||
埃爾曼多夫撕裂強度 | MD | ASTM D-1922 | 5 | N/mm2 | ||
TD | ASTM D-1922 | 96 | N/mm2 | |||
沖擊強度 | 35 | g |