斷裂伸長率 | 550% | 拉伸強度 | 64MPa | 密度 | 0.952g/cm3 |
熔體流動速率 | 0.05g/10min | 維卡軟化點 | 125℃ | 用途級別 | 薄膜級 |
規(guī)格級別 | 薄膜 |
|
產(chǎn)品簡述
斷裂伸長率 | 550% | 拉伸強度 | 64MPa | 密度 | 0.952g/cm3 |
熔體流動速率 | 0.05g/10min | 維卡軟化點 | 125℃ | 用途級別 | 薄膜級 |
規(guī)格級別 | 薄膜 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | HLMI | ASTM D-1238 | 8.5 | g/10min | ||
密度 | ASTM D-1505 | 0.952 | g/cm3 | |||
熔體流動速率 | ASTM D-1238 | 0.05 | g/10min | |||
機械性能 | Elmendorf斷裂強度 | MD | ASTM D-1922 | 12 | g | |
TD | ASTM D-1922 | 60 | g | |||
拉伸屈服強度 | MD | ASTM D-882 | 33 | MPa | ||
TD | ASTM D-882 | 40 | MPa | |||
Dart沖擊強度 | F50 | ASTM D-1709 | 180 | g | ||
拉伸斷裂伸長率 | MD | ASTM D-882 | 400 | % | ||
TD | ASTM D-882 | 550 | % | |||
1%割線模量 | MD | ASTM D-882 | 1250 | MPa | ||
TD | ASTM D-882 | 1500 | MPa | |||
拉伸斷裂強度 | MD | ASTM D-882 | 66 | MPa | ||
TD | ASTM D-882 | 64 | MPa | |||
熱性能 | 維卡軟化點 | ASTM D-1525 | 125 | ℃ |