斷裂伸長率 | 950% | 拉伸強(qiáng)度 | 29.5MPa | 密度 | 0.946g/cm3 |
熔體流動速率 | 0.3g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
|
產(chǎn)品簡述
斷裂伸長率 | 950% | 拉伸強(qiáng)度 | 29.5MPa | 密度 | 0.946g/cm3 |
熔體流動速率 | 0.3g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
詳細(xì)數(shù)據(jù)
訂購指南
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.946 | g/cc | ||
熔體流動速率 | 2.16kg | ASTM D-1238 | 0.30 | g/10min | ||
機(jī)械性能 | Dart沖擊強(qiáng)度 | F50,38mm Dart,66cm height | ASTM D-1709 | 2.0 | g/μm | |
斷裂伸長率 | MD | ASTM D-882 | 750 | % | ||
TD | ASTM D-882 | 950 | % | |||
撕裂強(qiáng)度 | MD | ASTM D-1922 | 0.8 | g/μm | ||
TD | ASTM D-1922 | 13.0 | g/μm | |||
屈服拉伸強(qiáng)度 | MD | ASTM D-882 | 26.5 | MPa | ||
TD | ASTM D-882 | 29.5 | MPa | |||
最終拉伸強(qiáng)度 | MD | ASTM D-882 | 55 | MPa | ||
TD | ASTM D-882 | 50 | MPa |