斷裂伸長率 | 5% | 拉伸強度 | 37.2MPa | 密度 | 0.958g/cm3 |
熔體流動速率 | 0.45g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 46 |
|
產品簡述
斷裂伸長率 | 5% | 拉伸強度 | 37.2MPa | 密度 | 0.958g/cm3 |
熔體流動速率 | 0.45g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 46 |
詳細數據
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數據 | 數據單位 | ||
基本性能 | 熔體流動速率 | ASTM D-1238 | 0.45 | g/10min | ||
熔體流動速率 | 190℃/21.6kg | ASTM D-1238 | 30 | g/10min | ||
密度 | ??松梨诜? | 0.958 | g/cm3 | |||
機械性能 | 屈服拉伸強度 | MD | ASTM D-882 | 34.3 | MPa | |
TD | ASTM D-882 | 19 | MPa | |||
斷裂拉伸強度 | MD | ASTM D-882 | 73.8 | MPa | ||
TD | ASTM D-882 | 37.2 | MPa | |||
斷裂伸長率 | MD | ASTM D-882 | 430 | % | ||
TD | ASTM D-882 | 5 | % | |||
切割模量 | MD | 1% | ASTM D-882 | 1150 | MPa | |
TD | 1% | ASTM D-882 | 1731 | MPa | ||
落鏢沖擊強度 | ASTM D-1709A | <46 | g | |||
埃爾曼多夫撕裂強度 | MD | ASTM D-1922 | 9 | g | ||
TD | ASTM D-1922 | 800 | g |