斷裂伸長率 | 1012% | 拉伸強度 | 37MPa | 密度 | 0.944g/cm3 |
熔體流動速率 | 0.58g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 115 |
|
產(chǎn)品簡述
斷裂伸長率 | 1012% | 拉伸強度 | 37MPa | 密度 | 0.944g/cm3 |
熔體流動速率 | 0.58g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 115 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 熔體流動速率 | 190℃/5.0kg | ASTM D-1238 | 0.58 | g/10min | |
熔體流動速率 | 190℃/21.6kg | ASTM D-1238 | 11.5 | g/10min | ||
密度 | ASTM D-1505 | 0.944 | g/cm3 | |||
機械性能 | 斷裂拉伸強度 | ASTM D-638 | 37 | MPa | ||
彎曲模量 | ASTM D-790 | 844 | MPa | |||
最終強度 | MD | ASTM D-882 | 60 | MPa | ||
TD | ASTM D-882 | 52 | MPa | |||
斷裂伸長率 | MD | ASTM D-882 | 667 | % | ||
TD | ASTM D-882 | 1012 | % | |||
屈服拉伸強度 | MD | ASTM D-882 | 20 | MPa | ||
TD | ASTM D-882 | 24 | MPa | |||
缺口沖擊強度 | ASTM D-1709 | 115 | gf/50%F | |||
埃爾曼多夫撕裂強度 | MD | ASTM D-1922 | 5 | kgf/cm | ||
TD | ASTM D-1922 | 64 | kgf/cm | |||
穿刺強度 | Braskem Method | 75 | J/M | |||
熱性能 | 維卡軟化點 | ASTM D-1525 | 123 | ℃ | ||
其它性能 | 最小推薦厚度 | 13 | μm |