拉伸強(qiáng)度 | 38MPa | 密度 | 1.04g/cm3 | 熔體流動速率 | 3g/10min |
缺口沖擊強(qiáng)度 | 75 | 成型收縮率 | 0.6% | 特性級別 | 阻燃級,抗靜電 |
|
產(chǎn)品簡述
拉伸強(qiáng)度 | 38MPa | 密度 | 1.04g/cm3 | 熔體流動速率 | 3g/10min |
缺口沖擊強(qiáng)度 | 75 | 成型收縮率 | 0.6% | 特性級別 | 阻燃級,抗靜電 |
詳細(xì)數(shù)據(jù)
訂購指南
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
物理性能 | 熔體流動速率 | 200℃/5Kg | ASTM D-1238 | 3 | g/10min |
成型收縮率 | ASTM D-955 | 0.4~0.8 | % | ||
比重 | ASTM D-792 | 1.04 | |||
機(jī)械性能 | 延伸率 | ASTM D-638 | 40 | % | |
抗張強(qiáng)度 | ASTM D-638 | 380 | kg/cm2 | ||
彎曲彈性率 | ASTM D-790 | 650 | kg/cm2 | ||
沖擊強(qiáng)度 | Notched 1/4" | ASTM D-256 | 5 | Kg/cm/cm | |
沖擊強(qiáng)度 | Notched1/8" | ASTM D-256 | 75 | Kg/cm/cm | |
洛氏硬度 | R-Scale | ASTM D-785 | 110 | ||
撓曲模量 | ASTM D-790 | 27.000 | kg/cm2 | ||
電氣性能 | HWI | UL 746A | 3 | PLC | |
抗弧光 | ASTM D-495 | 5 | PLC | ||
HAI | UL 746A | 0 | PLC | ||
CTI | UL 746A | 1 | PLC | ||
HVTR | UL 746A | 3 | PLC | ||
熱性能 | 維卡軟化點(diǎn) | 1.000g | ASTM D-1525 | 101 | ℃ |
燃燒率 | 1/16" | UL 94 | HB | ||
熱變形溫度 | Unannealed18.5g/cm2,1/4" | ASTM D-648 | 80 | ℃ | |
燃燒率 | 1/8" | UL 94 | HB | ||
燃燒率 | 1/8" | IEC 707 | FH3-30 | mm/min |