密度 | 1.04g/cm3 | 熔體流動速率 | 4g/10min | 吸水率 | 0.05% |
缺口沖擊強(qiáng)度 | 89.1 | 成型收縮率 | 0.45% |
|
產(chǎn)品簡述
密度 | 1.04g/cm3 | 熔體流動速率 | 4g/10min | 吸水率 | 0.05% |
缺口沖擊強(qiáng)度 | 89.1 | 成型收縮率 | 0.45% |
詳細(xì)數(shù)據(jù)
訂購指南
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
基本性能 | 熔體流動速率 | 200℃/5kg | ASTM D-1238 | 4.0 | g/10min |
吸水率 | 24hr | ASTM D-570 | 0.050 | % | |
物理性能 | 比重 | ASTM D-792 | 1.04 | g/cm3 | |
模具收縮率 | Flow | ASTM D-955 | 0.30-0.60 | % | |
機(jī)械性能 | 拉伸屈服強(qiáng)度 | ASTM D-638 | 32.3 | MPa | |
拉伸屈服伸長率 | ASTM D-638 | 35 | % | ||
彎曲模量 | ASTM D-790 | 2150 | MPa | ||
彎曲屈服強(qiáng)度 | ASTM D-790 | 41.1 | MPa | ||
IZOD缺口沖擊強(qiáng)度 | 3.20mm | ASTM D-256 | 89.1 | J/m | |
洛氏硬度 | ASTM D-785 | 75 | L scale | ||
電氣性能 | 體積電阻率 | ASTM D-257 | 1.0E+16 | ohm.cm | |
介電強(qiáng)度 | ASTM D-149 | 17.7 | KV/mm | ||
介電常數(shù) | 1E+6Hz | ASTM D-150 | 2.600 | ||
熱性能 | 熱變形溫度 | 1.80MPa,未退火 | ASTM D-648 | 82.8 | ℃ |
維卡軟化溫度 | ASTM D-1525 | 100 | ℃ | ||
燃燒性 | 1.59mm | UL 94 | HB | ||
燃燒性 | 3.18mm | UL 94 | HB | ||
燃燒性 | 6.35mm | UL 94 | HB | ||
RTI Str | 1.59mm | UL 746 | 50.0 | ℃ | |
RTI Str | 3.18mm | UL 746 | 50.0 | ℃ | |
RTI Str | 6.35mm | UL 746 | 50.0 | ℃ | |
RTI Imp | 1.59mm | UL 746 | 50.0 | ℃ | |
RTI Imp | 3.18mm | UL 746 | 50.0 | ℃ | |
RTI Imp | 6.35mm | UL 746 | 50.0 | ℃ | |
RTI Elec | 1.59mm | UL 746 | 50.0 | ℃ | |
RTI Elec | 3.18mm | UL 746 | 50.0 | ℃ | |
RTI Elec | 6.35mm | UL 746 | 50.0 | ℃ |