斷裂伸長率 | 770% | 拉伸強度 | 17MPa | 密度 | 0.923g/cm3 |
熔體流動速率 | 0.3g/10min | 規(guī)格級別 | 薄膜級 | 缺口沖擊強度 | 380 |
|
產(chǎn)品簡述
斷裂伸長率 | 770% | 拉伸強度 | 17MPa | 密度 | 0.923g/cm3 |
熔體流動速率 | 0.3g/10min | 規(guī)格級別 | 薄膜級 | 缺口沖擊強度 | 380 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 |
密度 | ASTM D-1505 | 0.923 | g/cm3 | |
斷裂拉伸強度 | 50mm/min | ASTM D-638 | 175 | kg/cm2 |
延伸率(MD) | ASTM D-882 | 460 | % | |
延伸率(TD) | ASTM D-882 | 660 | % | |
斷裂延伸率 | 50mm/min | ASTM D-638 | 770 | % |
屈服拉伸強度 | 50mm/min | ASTM D-638 | 120 | kg/cm2 |
斷裂拉伸強度(MD) | ASTM D-882 | 240 | kg/cm2 | |
斷裂拉伸強度(TD) | ASTM D-882 | 250 | kg/cm2 | |
維卡軟化點 | 1kg | ASTM D-1525 | 93 | ℃ |
Dart Drop沖擊強度 | ASTM D-1709 | 380 | g | |
霧度 | ASTM D-1003 | 10 | % | |
彎曲硬度 | ASTM D-747 | 2600 | kg/cm2 | |
融點 | Dsc | ASTM SGC | 111 | ℃ |
摩擦系數(shù) | ASTM D-1894 | >1.0 | ||
熔融指數(shù) | 190℃,2.16kg | ASTM D-1238 | 0.3 | g/10min |
脆化溫度 | ASTM D-746 | ℃ | ||
Dart Drop沖擊強度 | ASTM D-1709 | 380 | g |