斷裂伸長率 | 740% | 拉伸強度 | 15MPa | 密度 | 0.921g/cm3 |
熔體流動速率 | 8g/10min | 規(guī)格級別 | 薄膜級 | 缺口沖擊強度 | 120 |
|
產(chǎn)品簡述
斷裂伸長率 | 740% | 拉伸強度 | 15MPa | 密度 | 0.921g/cm3 |
熔體流動速率 | 8g/10min | 規(guī)格級別 | 薄膜級 | 缺口沖擊強度 | 120 |
詳細(xì)數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 |
密度 | ASTM D-1505 | 0.921 | g/cm3 | |
斷裂延伸率 | 50mm/min | ASTM D-638 | 740 | % |
Dart Drop沖擊強度 | ASTM D-1709 | 120 | g | |
斷裂拉伸強度(MD) | ASTM D-882 | 200 | kg/cm2 | |
斷裂拉伸強度(TD) | ASTM D-882 | 190 | kg/cm2 | |
延伸率(MD) | ASTM D-882 | 400 | % | |
延伸率(TD) | ASTM D-882 | 600 | % | |
斷裂拉伸強度 | 50mm/min | ASTM D-638 | 160 | kg/cm2 |
Dart Drop沖擊強度 | ASTM D-1709 | 120 | g | |
屈服拉伸強度 | 50mm/min | ASTM D-638 | 105 | kg/cm2 |
維卡軟化點 | 1kg | ASTM D-1525 | 89 | ℃ |
摩擦系數(shù) | ASTM D-1894 | 0.3 | ||
熔融指數(shù) | 190℃,2.16kg | ASTM D-1238 | 8 | |
彎曲硬度 | ASTM D-747 | 2200 | ||
脆化溫度 | ASTM D-746 | |||
熔點 | Dsc | ASTM SGC | 109 |