斷裂伸長率 | 650% | 拉伸強度 | 13MPa | 密度 | 0.923g/cm3 |
熔體流動速率 | 1.3g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 120 | 加工級別 | 吹塑級 |
|
產(chǎn)品簡述
斷裂伸長率 | 650% | 拉伸強度 | 13MPa | 密度 | 0.923g/cm3 |
熔體流動速率 | 1.3g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 120 | 加工級別 | 吹塑級 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 熔體流動速率 | ASTM D-1238 | 1.3 | g/10min | ||
密度 | ASTM D-1505 | 0.923 | g/cc | |||
機械性能 | 拉伸抗熱強度 | MD | ASTM D-1004 | 98 | kg/cm | |
TD | ASTM D-1004 | 95 | kg/cm | |||
下降沖擊強度 | ASTM D-1709 | 120 | g | |||
斷裂拉伸強度 | MD | ASTM D-882 | 235 | kg/cm2 | ||
TD | ASTM D-882 | 220 | kg/cm2 | |||
斷裂伸長率 | MD | ASTM D-882 | 400 | % | ||
TD | ASTM D-882 | 550 | % | |||
延伸率(破斷點) | ASTM D-638 | 650 | % | |||
抗張強度(破斷點) | ASTM D-638 | 140 | kg/cm2 | |||
熱性能 | 維卡軟化點 | ASTM D-1525 | 90 | ℃ | ||
熔點 | ASTM D-2117 | 111 | ℃ | |||
其它性能 | 混濁度 | ASTM D-1009 | 8.0 | % | ||
光澤度 | 45 | ASTM D-2457 | 70 | % | ||
厚度 | HCC | 0.06 | ㎜ |