性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 密度 | ASTM D-792 | 0.924 | g/cm3 | ||
熔體流動速率 | ASTM D-1238 | 0.88 | g/10min | |||
薄膜厚度 | 50.8 | μ | ||||
機(jī)械性能 | 切割模量 | MD | ASTM D-882 | 202 | MPa | |
TD | ASTM D-882 | 228 | MPa | |||
屈服拉伸強(qiáng)度 | MD | ASTM D-882 | 11.7 | MPa | ||
TD | ASTM D-882 | 12.2 | MPa | |||
斷裂拉伸強(qiáng)度 | MD | ASTM D-882 | 21.5 | MPa | ||
TD | ASTM D-882 | 17.9 | MPa | |||
斷裂伸長率 | MD | ASTM D-882 | 370 | % | ||
TD | ASTM D-882 | 570 | % | |||
落鏢沖擊強(qiáng)度 | ASTM D-1709 | 120 | g | |||
埃爾曼多夫撕裂強(qiáng)度 | MD | ASTM D-1922 | 430 | g | ||
TD | ASTM D-1922 | 480 | g | |||
熱性能 | 維卡軟化點(diǎn) | ASTM D-1525 | 97.2 | ℃ | ||
熔點(diǎn) | DSC | 112 | ℃ | |||
光學(xué)性能 | 光澤度 | ASTM D-2457 | 76 | |||
霧度 | ASTM D-1003 | 7.0 | % |