斷裂伸長(zhǎng)率 | 600% | 拉伸強(qiáng)度 | 18MPa | 密度 | 0.924g/cm3 |
熔體流動(dòng)速率 | 0.8g/10min | 彎曲模量 | 176MPa |
|
產(chǎn)品簡(jiǎn)述
斷裂伸長(zhǎng)率 | 600% | 拉伸強(qiáng)度 | 18MPa | 密度 | 0.924g/cm3 |
熔體流動(dòng)速率 | 0.8g/10min | 彎曲模量 | 176MPa |
詳細(xì)數(shù)據(jù)
訂購(gòu)指南
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.924 | g/cm3 | ||
熔體流動(dòng)速率 | ASTM D-1238 | 0.8 | g/10min | |||
機(jī)械性能 | 抗撕裂性 | MD | ASTM D-1922 | 45 | N/mm | |
TD | ASTM D-1922 | 60 | N/mm | |||
拉力降伏強(qiáng)度 | MD | ASTM D-882B | 100 | kg/cm2 | ||
TD | ASTM D-882B | 110 | kg/cm2 | |||
拉力降伏強(qiáng)度 | ASTM D-638 | 120 | kg/cm2 | |||
拉力斷裂強(qiáng)度 | ASTM D-638 | 170 | kg/cm2 | |||
硬度 | ASTM D-2240 | 54 | Shore D | |||
摩擦系數(shù) | ASTM D-1894 | >0.5 | ||||
落球行動(dòng)強(qiáng)度 | ASTM D-1709 | 260 | g | |||
彎曲模量 | ASTM D-790 | 1800 | kg/cm2 | |||
拉力斷裂伸長(zhǎng)率 | ASTM D-638 | 700 | % | |||
拉力斷裂伸長(zhǎng)率 | MD | ASTM D-882B | 380 | % | ||
TD | ASTM D-882B | 600 | % | |||
1%伸長(zhǎng)彈性系數(shù) | MD | ASTM D-882B | 1900 | kg/cm2 | ||
TD | ASTM D-882B | 2150 | kg/cm2 | |||
拉力斷裂強(qiáng)度 | MD | ASTM D-882B | 220 | kg/cm2 | ||
TD | ASTM D-882B | 190 | kg/cm2 | |||
熱性能 | 軟化點(diǎn) | ASTM D-1525 | 98 | ℃ | ||
熔點(diǎn) | DSC | 113 | ℃ | |||
脆化溫度 | ASTM D-746 | <-70 | ℃ | |||
其它性能 | 薄膜厚度 | ASTM D-1003 | 30~120 | µ | ||
濁度 | ASTM D-1003 | 10 | % | |||
光澤度45° | ASTM D-2457 | 70 | % |