斷裂伸長率 | 600% | 密度 | 0.924g/cm3 | 熔體流動速率 | 0.8g/10min |
維卡軟化點 | 98℃ | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 180 |
|
產(chǎn)品簡述
斷裂伸長率 | 600% | 密度 | 0.924g/cm3 | 熔體流動速率 | 0.8g/10min |
維卡軟化點 | 98℃ | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 180 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
其它性能 | 斷裂點伸長率 | MD | ASTM D-882B | 380 | % | |
TD | ASTM D-882B | 600 | % | |||
基本性能 | 熔體流動速率 | ASTM D-1238 | 0.8 | g/10min | ||
密度 | ASTM D-1505 | 0.924 | g/cm3 | |||
物理性能 | 薄膜厚度 | 30-120 | ||||
濁度 | ASTM D-1003 | 7.5 | % | |||
機械性能 | 斷裂點強度 | MD | ASTM D-882B | 220 | kg/cm2 | |
TD | ASTM D-882B | 190 | kg/cm2 | |||
1%伸長彈性系數(shù) | MD | ASTM D-882B | 1900 | kg/cm2 | ||
TD | ASTM D-882B | 2150 | kg/cm2 | |||
落球沖擊強度 | ASTM D-1709 | 180 | g | |||
降伏點強度 | MD | ASTM D-882B | 100 | kg/cm2 | ||
TD | ASTM D-882B | 110 | kg/cm2 | |||
熱性能 | 熔點 | DSC | 114 | ℃ | ||
脆化溫度 | ASTM D-746 | <-75 | ℃ | |||
軟化點 | ASTM D-1525 | 98 | ℃ | |||
其它性能 | 抗撕裂性 | MD | ASTM D-1922 | 45 | N/mm | |
TD | ASTM D-1922 | 60 | N/mm | |||
光澤度 | 45℃ | ASTM D-2457 | 65 | % | ||
摩擦系數(shù) | ASTM D-1894 | 0.11 |