斷裂伸長率 | 650% | 拉伸強度 | 13MPa | 密度 | 0.924g/cm3 |
熔體流動速率 | 2g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 65 |
|
產(chǎn)品簡述
斷裂伸長率 | 650% | 拉伸強度 | 13MPa | 密度 | 0.924g/cm3 |
熔體流動速率 | 2g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 65 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 熔體流動速率 | ASTM D-1238 | 2.0 | g/10min | ||
密度 | ASTM D-1505 | 0.924 | g/cm3 | |||
物理性能 | 霧度 | ASTM D-1003 | 4.5 | % | ||
光澤度 | 45℃ | ASTM D-2457 | 95 | |||
薄膜厚度 | HPS | 30 | μm | |||
機械性能 | 肖氏硬度 | ASTM D-2240 | 52 | D SCALE | ||
斷裂伸長率 | MD | ASTM D-882 | 300 | % | ||
TD | ASTM D-882 | 550 | % | |||
伸長彈性率 | ASTM D-638 | 1.350 | kg/cm2 | |||
斷裂伸長率 | ASTM D-638 | 650 | % | |||
落球沖擊強度 | ASTM D-1709A | 65 | g | |||
斷裂拉伸強度 | MD | ASTM D-882 | 270 | Kg/cm2 | ||
TD | ASTM D-882 | 240 | Kg/cm2 | |||
斷裂拉伸強度 | ASTM D-638 | 135 | kg/cm2 | |||
屈服拉伸強度 | ASTM D-638 | 96 | kg/cm2 | |||
熱性能 | 軟化點 | ASTM D-1525 | 95 | ℃ | ||
熔點 | HPC | 107 | ℃ |