斷裂伸長率 | 400% | 拉伸強度 | 11MPa | 密度 | 0.921g/cm3 |
熔體流動速率 | 0.38g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
脆化溫度 | -68℃ |
|
產(chǎn)品簡述
斷裂伸長率 | 400% | 拉伸強度 | 11MPa | 密度 | 0.921g/cm3 |
熔體流動速率 | 0.38g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
脆化溫度 | -68℃ |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 熔體流動速率 | ASTM D-1238 | 0.38 | g/10min | ||
密度 | ASTM D-792 | 0.921 | g/cm3 | |||
機械性能 | 屈服拉伸強度 | MD | ASTM D-882 | 10 | MPa | |
TD | ASTM D-882 | 11 | MPa | |||
最終強度 | MD | ASTM D-882 | 24 | MPa | ||
TD | ASTM D-882 | 22 | MPa | |||
斷裂伸長率 | MD | ASTM D-882 | 200 | % | ||
TD | ASTM D-882 | 400 | % | |||
沖擊強度 | ASTM D-1709 | 1.68 | gf/μm | |||
埃爾曼多夫撕裂強度 | MD | ASTM D-1922 | 4 | gf/μm | ||
TD | ASTM D-1922 | 16 | gf/μm | |||
熱性能 | 脆化溫度 | ASTM D-746 | -68 | ℃ | ||
光學性能 | 光澤度 | ASTM D-2457 | 70 | % |