斷裂伸長率 | 580% | 拉伸強度 | 14MPa | 密度 | 0.925g/cm3 |
熔體流動速率 | 0.8g/10min | 用途級別 | 薄膜級,食品級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 150 |
|
產(chǎn)品簡述
斷裂伸長率 | 580% | 拉伸強度 | 14MPa | 密度 | 0.925g/cm3 |
熔體流動速率 | 0.8g/10min | 用途級別 | 薄膜級,食品級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 150 |
詳細(xì)數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 密度 | 23°C | ASTM D-1505 | 0.925 | g/cm3 | |
熔體流動速率 | ASTM D-1238 | 0.8 | g/10min | |||
機(jī)械性能 | 破裂點張力 | MD | ASTM D-882 | 275 | kg/cm2 | |
TD | ASTM D-882 | 235 | kg/cm2 | |||
斷裂點伸張率 | MD | ASTM D-882 | 490 | % | ||
TD | ASTM D-882 | 600 | % | |||
屈服點張力 | ASTM D-638 | 115 | Kg/cm2 | |||
抗張強度 | ASTM D-638 | 145 | Kg/cm2 | |||
斷裂伸長率 | ASTM D-638 | 580 | % | |||
抗撕裂張度 | MD | ASTM D-1922 | 280 | g | ||
TD | ASTM D-1922 | 280 | g | |||
跌落沖擊強度 | ASTM D-1709 | 150 | g | |||
熱性能 | 維卡軟化點 | ASTM D-1525 | 97 | °C | ||
低溫脆化溫度 | ASTM D-746 | <-76 | °C |