斷裂伸長率 | 560% | 拉伸強度 | 23MPa | 密度 | 0.922g/cm3 |
熔體流動速率 | 0.75g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 4 |
|
產(chǎn)品簡述
斷裂伸長率 | 560% | 拉伸強度 | 23MPa | 密度 | 0.922g/cm3 |
熔體流動速率 | 0.75g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 4 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 熔體流動速率 | ASTM D-1238 | 0.75 | g/10min | ||
密度 | ASTM D-1505 | 0.922 | g/cm3 | |||
物理性能 | 光澤 | 60度 | ASTM D-2457 | 9 | ||
機械性能 | Elmendorf斷裂強度 | MD | ASTM D-1922 | 4 | ||
TD | ASTM D-1922 | 7 | ||||
斷裂伸長率 | MD | ASTM D-882 | 370 | % | ||
TD | ASTM D-882 | 560 | % | |||
屈服點 | ASTM D-882|ASTM D-882 | 12|12 | MPa|MPa | |||
斷裂拉伸 | MD | ASTM D-882 | 26 | MPa | ||
TD | ASTM D-882 | 23 | MPa | |||
Dart沖擊強度 | ASTM D-1709 | 4 | ||||
1%割線模量 | MD | ASTM D-882 | 220 | MPa | ||
TD | ASTM D-882 | 240 | MPa | |||
熱性能 | 維卡軟化點 | ASTM D-1525 | 98 | ℃ | ||
其它性能 | 混濁 | ASTM D-1003 | 6.5 | % |