斷裂伸長率 | 682% | 拉伸強(qiáng)度 | 21MPa | 密度 | 0.918g/cm3 |
熔體流動(dòng)速率 | 2g/10min | 維卡軟化點(diǎn) | 96℃ | 用途級別 | 薄膜級 |
規(guī)格級別 | 薄膜 |
|
產(chǎn)品簡述
斷裂伸長率 | 682% | 拉伸強(qiáng)度 | 21MPa | 密度 | 0.918g/cm3 |
熔體流動(dòng)速率 | 2g/10min | 維卡軟化點(diǎn) | 96℃ | 用途級別 | 薄膜級 |
規(guī)格級別 | 薄膜 |
詳細(xì)數(shù)據(jù)
訂購指南
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 密度 | ASTM D-792 | 0.9180 | g/cc | ||
機(jī)械性能 | 屈服拉伸強(qiáng)度 | MD | ASTM D-882 | 11 | MPa | |
TD | ASTM D-882 | 9 | MPa | |||
斷裂拉伸強(qiáng)度 | MD | ASTM D-882 | 40 | MPa | ||
TD | ASTM D-882 | 21 | MPa | |||
Dart 沖擊強(qiáng)度 | ASTM D-1709 | 66 | g | |||
刺穿強(qiáng)度 | ASTM DOW | 9 | J/cm3 | |||
熱性能 | 維卡軟化點(diǎn) | ASTM D-1525 | 96 | ℃ | ||
其它性能 | 斷裂伸長率 | MD | ASTM D-882 | 447 | % | |
TD | ASTM D-882 | 682 | % | |||
熔融指數(shù) | ASTM D-1238 | 2.0 | g/10min | |||
霧度 | ASTM D-1003 | 0.56 | % | |||
光澤度 | ASTM D-2457 | 151 | ||||
抗撕裂性 | MD | ASTM D-1992 | 37 | g | ||
TD | ASTM D-1992 | 370 | g | |||
拉伸模量 | MD | ASTM D-882 | 149 | MPa | ||
TD | ASTM D-882 | 147 | MPa | |||
透明度 | ASTM D-1746 | 99 | ||||
熔點(diǎn) | ASTM DOW | 104 | ℃ |