斷裂伸長(zhǎng)率 | 850% | 拉伸強(qiáng)度 | 35MPa | 密度 | 0.919g/cm3 |
熔體流動(dòng)速率 | 1g/10min | 用途級(jí)別 | 薄膜級(jí) | 規(guī)格級(jí)別 | 薄膜 |
缺口沖擊強(qiáng)度 | 10 |
|
產(chǎn)品簡(jiǎn)述
斷裂伸長(zhǎng)率 | 850% | 拉伸強(qiáng)度 | 35MPa | 密度 | 0.919g/cm3 |
熔體流動(dòng)速率 | 1g/10min | 用途級(jí)別 | 薄膜級(jí) | 規(guī)格級(jí)別 | 薄膜 |
缺口沖擊強(qiáng)度 | 10 |
詳細(xì)數(shù)據(jù)
訂購(gòu)指南
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
其它性能 | 拉伸斷裂強(qiáng)度 | MD | ASTM D-882 | 430 | Kg/cm2 | |
TD | ASTM D-882 | 360 | Kg/cm2 | |||
基本性能 | 密度 | ASTM D-1505 | 0.919 | g/cm3 | ||
熔體流動(dòng)速率 | ASTM D-1238 | 1 | g/10min | |||
機(jī)械性能 | 拉伸屈服強(qiáng)度 | MD | ASTM D-882 | 120 | Kg/cm2 | |
TD | ASTM D-882 | 110 | Kg/cm2 | |||
伸長(zhǎng)率 | MD | ASTM D-882 | 750 | % | ||
TD | ASTM D-882 | 850 | % | |||
撕裂強(qiáng)度 | MD | ASTM D-1004 | 5 | Kg/cm | ||
TD | ASTM D-1004 | 12 | Kg/cm | |||
抗沖擊強(qiáng)度 | ASTM D-3420 | 10 | Kg/cm | |||
撕裂彈性率 | MD | ASTM D-882 | 2,000 | Kg/cm2 | ||
TD | ASTM D-882 | 2,500 | Kg/cm2 | |||
熱性能 | 維卡軟化點(diǎn) | ASTM D-1525 | 102 | ℃ | ||
脆化溫度 | ASTM D-746 | <-70 | ℃ | |||
其它性能 | 霧度 | ASTM D-1003 | 23 | % | ||
薄膜厚度 | ASTM D-746 | 50 | µm |