斷裂伸長率 | 937% | 拉伸強度 | 19MPa | 密度 | 0.918g/cm3 |
熔體流動速率 | 1g/10min | 規(guī)格級別 | 吹塑擠出薄膜光學 |
|
產(chǎn)品簡述
斷裂伸長率 | 937% | 拉伸強度 | 19MPa | 密度 | 0.918g/cm3 |
熔體流動速率 | 1g/10min | 規(guī)格級別 | 吹塑擠出薄膜光學 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 |
熔體流動速率 | ASTM D-1238 | 1.0 | g/10min | |
磨擦系數(shù) | ASTM D-1505 | 0.918 | g/cm3 | |
斷裂拉伸強度 | ASTM D-882 | MD,TD,26,19 | MPa | |
斷裂伸長率 | ASTM D-882 | MD,TD,788,937 | % | |
切割模量 | 1% | ASTM D-882 | TD,MD,230,201 | MPa |
落鏢沖擊強度 | ASTM D-1709 | 102 | gf/50%F | |
埃爾曼多夫撕裂強度 | ASTM D-1922 | TD,MD,101,43 | kgf/cm | |
霧度 | ASTM D-1003 | 10.2 | % | |
光澤度 | ASTM D-2457 | 10.3 | % |