| 斷裂伸長率 | 5% | 密度 | 1.5g/cm3 | 彎曲強度 | 6107.84MPa |
| 吸水率 | 5.5% | 成型收縮率 | 0.1% | 特性級別 | 增強級 |
在線訂購支持
在線訂購說明
保障消費者權(quán)益，真正做到正品交易，杜絕假冒偽劣產(chǎn)品
021-58958519 13061808058(蔣先生) 13424755533(趙先生)
聯(lián)系上海松翰
| 021-58958519 | |
| 13061808058(蔣先生) | |
| 13424755533(趙先生) | |
| |
|
|
產(chǎn)品簡述
備注
備注:特性：玻纖增強45%
詳細數(shù)據(jù)
訂購指南
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 成型收縮率 | UBEmethod | 0.1 | % | |
| 吸水率 | ASTM D-570 | 5.5 | % | ||
| 成型收縮率 | UBEmethod | 0.5 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 1.50 | ||
| 機械性能 | 抗沖擊強度 | 23° | ASTM D-256 | 25 | kgf.cm/cm |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 115 | ||
| 抗沖擊強度 | 23° | ASTM D-256 | 15 | kgf.cm/cm | |
| 彎曲強度 | 23° | ASTM D-790 | 62300 | kgf/cm2 | |
| TABER磨耗率 | ASTM D-1044 | 18 | mg | ||
| 1%變形下的壓縮強度 | 23° | ASTM D-695 | 200 | kgf/cm2 | |
| 體積電阻率 | Ω.cm | ASTM D-257 | 1012 | ||
| 彎曲強度 | -30° | ASTM D-790 | 3700 | kgf/cm2 | |
| 斷裂下的延伸率 | 23° | ASTM D-638 | 4 | % | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 120 | ||
| 斷裂下的延伸率 | 23° | ASTM D-638 | 5 | % | |
| 屈服下的伸張強度 | 80° | ASTM D-638 | 1240 | kgf/cm2 | |
| 抗沖擊強度 | -30° | ASTM D-256 | 15 | kgf.cm/cm | |
| 屈服下的伸張強度 | 23° | ASTM D-638 | 2040 | kgf/cm2 | |
| 屈服下的伸張強度 | -30° | ASTM D-638 | 2700 | kgf/cm2 | |
| 1%變形下的壓縮強度 | 23° | ASTM D-695 | 310 | kgf/cm2 | |
| 屈服下的伸張強度 | 23° | ASTM D-638 | 1330 | kgf/cm2 | |
| 彎曲彈性率 | 80° | ASTM D-790 | 67000 | kgf/cm2 | |
| 擠剪強度 | 23° | ASTM D-732 | 960 | kgf/cm2 | |
| 抗沖擊強度 | -30° | ASTM D-256 | 12 | kgf.cm/cm | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 105 | ||
| 彎曲彈性率 | 23° | ASTM D-790 | 120000 | kgf/cm2 | |
| 擠剪強度 | 23° | ASTM D-732 | 700 | kgf/cm2 | |
| 電氣性能 | 介電常數(shù) | 103HZ | ASTM D-150 | 4.2 | |
| 抗電弧強度 | ASTM D-495 | 138 | S | ||
| 體積電阻率 | ASTM D-257 | 1012 | Ω.cm | ||
| 介電損耗 | ASTM D-150 | 106HZ | 0.01 | ||
| IEC電路 | UL746 | 500 | V | ||
| 介電常數(shù) | 106HZ | ASTM D-150 | 3.9 | ||
| 介電常數(shù) | 60HZ | ASTM D-150 | 4.3 | ||
| 介電損耗 | 60HZ | ASTM D-150 | 0.01 | ||
| 介電損耗 | 103HZ | ASTM D-150 | 0.01 | ||
| 熱性能 | 殘性熱膨脹系數(shù) | ASTM D-696 | 2 | X的10-5cm/cm/°C | |
| 燃燒率 | UL94 | HB | |||
| 熔點 | DSC | 215-225 | °C | ||
| 熱變形溫度 | 18.6kgf/cm2 | ASTM D-648 | 215 | °C | |