性能項(xiàng)目 |
試驗(yàn)條件[狀態(tài)] |
測(cè)試方法 |
測(cè)試數(shù)據(jù) |
數(shù)據(jù)單位 |
物理性能 |
收縮率 |
平行流動(dòng)方向 |
ASTM D955 |
0.016 |
cm/cm |
收縮率 |
垂直流動(dòng)方向 |
ASTM D955 |
0.016 |
cm/cm |
機(jī)械性能 |
彎曲模量 |
90 °C, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant |
ASTM D790 |
331 |
Mpa |
彎曲模量 |
(-40 °C, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant |
ASTM D790 |
3000 |
Mpa |
彎曲模量 |
23 °C, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant |
ASTM D790 |
2410 |
Mpa |
彎曲模量 |
149 °C, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant |
ASTM D790 |
234 |
Mpa |
彎曲強(qiáng)度 |
90 °C, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I |
ASTM D790 |
13 |
Mpa |
彎曲強(qiáng)度 |
(-40 °C, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I |
ASTM D790 |
120 |
Mpa |
彎曲強(qiáng)度 |
23 °C, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I |
ASTM D790 |
80 |
Mpa |
彎曲強(qiáng)度 |
149 °C, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I |
ASTM D790 |
8 |
Mpa |
斷裂點(diǎn)伸長(zhǎng)率 |
- |
90 °C, 0.00 mm, Compression Molded, Type I |
ASTM D638 |
300 |
% |
- |
-40 °C, 0.00 mm, Compression Molded, Type I |
ASTM D638 |
11 |
% |
- |
23 °C, 0.00 mm, Compression Molded, Type I |
ASTM D638 |
300 |
% |
- |
150 °C, 0.00 mm, Compression Molded, Type I |
ASTM D638 |
300 |
% |
非缺口沖擊強(qiáng)度 |
- |
-40 °C, 0.00 mm |
ASTM D256 |
No Break |
J/m |
- |
23 °C, 0.00 mm |
ASTM D256 |
No Break |
J/m |
熱性能 |
熔點(diǎn) |
|
DSC |
225 |
℃ |
阻燃性 |
- |
3.00 mm |
UL94 |
HB |
|
- |
1.5mm |
UL94 |
HB |
|
- |
0.81mm |
UL94 |
HB |
|
其它性能 |
極限氧指數(shù) |
3.20 mm |
ASTM D2863 |
22 |
% |