用途級別 | 醫(yī)用級,汽車部件 | 規(guī)格級別 | 脫模醫(yī)用注塑 | 加工級別 | 注塑級,脫模級 |
特性級別 | 耐水解,阻燃級,抗靜電 |
|
產(chǎn)品簡述
用途級別 | 醫(yī)用級,汽車部件 | 規(guī)格級別 | 脫模醫(yī)用注塑 | 加工級別 | 注塑級,脫模級 |
特性級別 | 耐水解,阻燃級,抗靜電 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
物理性能 | 比重 | ASTM D792,ISO 1183/A | 1.20 | g/cm3 | |
熔流率 | 300℃/1.2kg | ASTM D1238,ISO 1133 | 10 | g/10min | |
流動收縮率 | ASTM D955 | 0.50-0.70 | % | ||
流量收縮率 | ISO 294-4 | 0.50-0.70 | % | ||
吸水率 | 23℃,24hr | ASTM D570,ISO 62 | 0.15 | % | |
平衡,23℃,50%RH | ASTM D570,ISO 62 | 0.32 | % | ||
洛氏硬度 | M計秤 | ASTM D785 | 72 | ||
R計秤 | ASTM D785 | 118 | |||
機械性能 | 拉伸模量 | ASTM D638 | 2210 | MPa | |
ISO 527-2/50 | 2300 | MPa | |||
屈服抗張強度 | ASTM D638 | 62.1 | MPa | ||
屈服抗張強度 | ISO 527-2/50 | 62.0 | MPa | ||
斷裂抗張強度 | ASTM D638 | 68.3 | MPa | ||
斷裂抗張強度 | ISO 527-2/50 | 68.0 | MPa | ||
屈服伸長率 | ASTM D638 | 6.0 | % | ||
屈服伸長率 | ISO 527-2/50 | 6.0 | % | ||
斷裂伸長率 | ASTM D638 | 150 | % | ||
斷裂伸長率 | ISO 527-2/50 | 150 | % | ||
彎曲模量 | ASTM D790 | 2410 | MPa | ||
彎曲模量 | ISO 178 | 2400 | MPa | ||
彎曲強度 | ASTM D790 | 96.5 | MPa | ||
彎曲強度 | ISO 178 | 98.0 | MPa | ||
耐磨耗性 | ASTM D1044 | 45 | % | ||
簡支梁缺口沖擊強度 | 23℃ | ISO 179/1eA | 35 | kJ/cm2 | |
懸壁梁缺口沖擊強度 | 23℃ | ASTM D256 | 750 | J/m |
|
23℃ | ISO 180/A | 78 | kJ/cm2 | ||
無缺口伊佐德沖擊強度 | 23℃ | ASTM D256,ISO 180 | 無斷裂 | ||
裝有測量儀表的落鏢沖擊 | 23℃,總能量 | ASTM D3763 | 81.3 | J | |
拉伸沖擊強度 | ASTM D1822 | 378 | kJ/cm2 | ||
熱性能 | 熱變形溫度 | 0.45MPa,退火 | ASTM D648,ISO 75-2/B | 140 | ℃ |
1.8MPa,未退火 | ASTM D648 | 122 | ℃ | ||
1.8MPa,未退火 | ISO 75-2/A | 121 | ℃ | ||
1.8MPa,退火 | ASTM D648,ISO 75-2/A | 137 | ℃ | ||
維卡軟化溫度 | ASTM D1525 | 148 | ℃ | ||
ISO 306/B50 | 143 | ℃ | |||
流動線形膨脹系數(shù) | -40到82℃ | ASTM D696 | 0.000068 | cm/cm/℃ | |
電氣性能 | 體積電阻率 | ASTM D257 | 2.0E+17 | ohm.cm | |
介電強度 | ASTM D149,IEC 60243-1 | 17 | kV/mm | ||
介電常數(shù) | 60Hz | ASTM D150 | 3.00 | ||
1 MHz | ASTM D150 | 3.00 | |||
耗散因數(shù) | 50Hz | ASTM D150 | 0.0010 | ||
1 MHz | ASTM D150 | 0.0020 | |||
光學(xué)性能 | 折射率 | ASTM D542,ISO 489 | 1.586 | ||
透射率 | ASTM D1003 | 89.0 | % | ||
霧度 | ASTM D1003 | 1.0 | % |