密度 | 1.41g/cm3 | 熔體流動速率 | 5g/10min | 吸水率 | 0.22% |
缺口沖擊強度 | 6.5 | 成型收縮率 | 2% | 加工級別 | 注塑級 |
特性級別 | 耐候 |
|
產(chǎn)品簡述
密度 | 1.41g/cm3 | 熔體流動速率 | 5g/10min | 吸水率 | 0.22% |
缺口沖擊強度 | 6.5 | 成型收縮率 | 2% | 加工級別 | 注塑級 |
特性級別 | 耐候 |
詳細(xì)數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
物理性能 | 比重 | ASTM D-792 | 1.41 | |||
吸收率 | 23℃,60%RH | ASTM D-570 | 0.22 | % | ||
機(jī)械性能 | 曲折彈性率 | 23℃ | ASTM D-790 | 2.62 | ×104kgf/cm2 | |
斷裂強度 | t2mm | ASTM D-732 | 560 | kgf.cm/cm2 | ||
拉伸沖擊強度 | t3.2mm S type | ASTM D-1822 | 110 | kgf.cm/cm2 | ||
120D沖擊強度 | Notch t3.2mm | ASTM D-256 | 6.5 | kgf.cm/cm | ||
伸縮率 | 23℃ | ASTM D-638 | 60 | % | ||
彎曲強度 | 23℃ | ASTM D-790 | 900 | kgf.cm/cm2 | ||
拉伸強度 | 23℃ | ASTM D-638 | 620 | kgf.cm/cm2 | ||
洛氏硬度 | ASTM D-785 | M80 | M scale | |||
電氣性能 | 體積電阻率 | ASTM D-257 | 1×1014 | Ω.cm | ||
耐電壓 | ASTM D-149 | 19 | MV/m | |||
個質(zhì)損耗系數(shù) | 106HZ | ASTM D-150 | 0.007 | |||
導(dǎo)電率 | 106HZ | ASTM D-150 | 3.7 | |||
表面電阻率 | ASTM D-257 | 1×1016 | Ω | |||
熱性能 | 熔體流動速率 | ASTM D-1238 | 6 | g/10min | ||
熔點 | 10℃/min | DSC Method | 165 | ℃ | ||
熱變形溫度 | 4.6kgf/cm2 | ASTM D-648 | 158 | ℃ | ||
18.6kgf/cm2 | ASTM D-648 | 110 | ℃ | |||
線膨脹系數(shù) | 20C°-80C | ASTM D-696 | 13 | ×10-5cm/cm/℃ | ||
燃燒性 | t0.8mm | UL 94 | HB | |||
其它性能 | 成型收縮率 | t3mm,直徑100mm | 2.0 | % |