斷裂伸長率 | 45% | 拉伸強(qiáng)度 | 61MPa | 彎曲強(qiáng)度 | 98MPa |
硬度 | 82 | 彎曲模量 | 2597MPa |
|
產(chǎn)品簡述
斷裂伸長率 | 45% | 拉伸強(qiáng)度 | 61MPa | 彎曲強(qiáng)度 | 98MPa |
硬度 | 82 | 彎曲模量 | 2597MPa |
詳細(xì)數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 |
吸水率 | ASTM D-570 | 0.22 | % | |
Taber磨耗量 | ASTM D-1044 | 14 | mg/1000cycles | |
比重 | ASTM D-792 | 1.41 | ||
模縮系數(shù) | 18~21 | cm/cm×0.0001 | ||
伸長率 | ASTM D-638 | 45 | % | |
沖擊強(qiáng)度(無缺口) | ASTM D-256 | 70 | kg.cm/cm | |
沖擊強(qiáng)度(缺口) | ASTM D-256 | 6.0 | kg.cm/cm | |
砦擠系數(shù)(動) | ASTM D-1894 | 0.16 | ||
砦擠系數(shù)(靜) | ASTM D-1894 | 0.12 | ||
張力 | ASTM D-638 | 625 | kg/cm2 | |
縮性熱伸張系數(shù) | ASTM D-696 | 10×0.000001 | mm/mm/C | |
彎曲模量 | ASTM D-790 | 26500 | kg/cm2 | |
洛氏硬度 | ASTM D-785 | 82 | M | |
彎曲強(qiáng)度 | ASTM D-790 | 1000 | kg/cm2 | |
抗表面性 | ASTM D-257 | 1×1016 | Ω | |
抗弧性 | ASTM D-495 | 240 | Sec | |
介電強(qiáng)度 | ASTM D-149 | 24 | KV/mm | |
抗體積性 | ASTM D-257 | 1×1014 | Ω.cm | |
介電定數(shù) | ASTM D-150 | 3.8 | ||
誘電正接 | ASTM D-150 | 0.007 | ||
熱變形溫度 | 4.6kg/cm2 | ASTM D-648 | 160 | C |
燃燒性 | 1/32" | HB | ||
熱變形溫度 | 18kg/cm2 | ASTM D-648 | 110 | C |