拉伸強(qiáng)度 | 380MPa | 密度 | 0.903g/cm3 | 熔體流動速率 | 11g/10min |
缺口沖擊強(qiáng)度 | 2.5 | 成型收縮率 | 1.7% |
|
產(chǎn)品簡述
拉伸強(qiáng)度 | 380MPa | 密度 | 0.903g/cm3 | 熔體流動速率 | 11g/10min |
缺口沖擊強(qiáng)度 | 2.5 | 成型收縮率 | 1.7% |
詳細(xì)數(shù)據(jù)
訂購指南
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
基本性能 | 密度 | ASTM D-792 | 0.903 | g/cm3 | |
熔體流動速率 | ASTM D-1238 | 11.0 | g/10min | ||
物理性能 | 霧度 | ASTM D-1003 | <2 | % | |
機(jī)械性能 | Young's Modulus | ASTM D-882 | 9 | Mpa | |
斷裂伸長率 | ASTM D-638 | >500 | % | ||
IZOD沖擊強(qiáng)度 | ASTM D-256 | 2.5 | kg.cm/cm | ||
彎曲模量 | ASTM D-790A | 16 | Mpa | ||
摩擦系數(shù) | ASTM D-1894 | 0.5 | - | ||
抗張強(qiáng)度(屈服) | ASTM D-638 | 380 | Mpa | ||
洛氏硬度 | ASTM D-785 | 105 | R scale | ||
Mold Shinkage (MD/TD) | ASTM D-955 | 1.5-1.9 | % | ||
延伸率(屈服) | ASTM D-638 | 10 | % | ||
熱性能 | 維卡軟化點(diǎn) | ASTM D-1525B | 152 | ℃ | |
熱變形溫度 | ASTM D-648 | 125 | ℃ | ||
Heat Sealing Temp | LG-Caltex | 150 | ℃ |