性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
基本性能 | 比重 | ASTM D1505 | 1.33 | g/cm3 | |
熔體質(zhì)量流動(dòng)速率 | 343°C, 2.16 kg | ASTM D1238 | 6.5 | g/10min | |
成型收縮率 | ASTM D955 | 0.4 | % | ||
機(jī)械性能 | 拉伸強(qiáng)度 | ASTM D638 | 78 | MPa | |
拉伸伸長(zhǎng)率 | ASTM D638 | 4 | % | ||
拉伸模量 | ASTM D638 | 3700 | MPa | ||
彎曲強(qiáng)度 | ASTM D790 | 128 | MPa | ||
彎曲模量 | ASTM D790 | 3800 | MPa | ||
IZOD缺口沖擊強(qiáng)度 | ASTM D256 | 4.8 | KJ/m2 | ||
拉伸沖擊強(qiáng)度 | ASTM D1822 | 100 | KJ/m2 | ||
電氣性能 | 絕緣強(qiáng)度 | ASTM D149 | 19 | kV/mm | |
體積電阻 | ASTM D257 | 3×1016 | Ω·cm | ||
介電常數(shù) | 60 Hz | ASTM D150 | 3.18 | ||
介電常數(shù) | 1000000 Hz | ASTM D150 | 3.15 | ||
介質(zhì)損耗因數(shù) | 60 Hz | ASTM D150 | 0.0007 | ||
介質(zhì)損耗因數(shù) | 1000000 Hz | ASTM D150 | 0.0060 | ||
熱性能 | 熱變形溫度 | 1.82MPa | ASTM D648 | 179 | ℃ |
阻燃性 | UL94 | HB | 級(jí) |