性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
物理性能 | 比重 | ASTM D792 | 1.26 | g/cm3 | |
流動(dòng)熔流率 | 230℃/2.16kg | ASTM D1238 | 16 | g/10min | |
流動(dòng)收縮率 | 2.00mm | ASTM D955 | 1.5 | % | |
平衡吸水率 | 23℃,65%RH | ASTM D570 | 0.34 | % | |
硬度計(jì)硬度 | 支撐 D | ASTM D2240 | 60 | ||
機(jī)械性能 | 屈服抗張強(qiáng)度 | ASTM D638 | 40.0 | MPa | |
斷裂伸長率 | ASTM D638 | 540 | % | ||
彎曲模量 | ASTM D790 | 274 | MPa | ||
壓縮模量 | ASTM D695 | 21.1 | MPa | ||
抗泰伯磨耗 | 1000 Cycles | ASTM D1044 | 10.0 | mg | |
拉伸應(yīng)力 | 50%應(yīng)變 | ASTM D412 | 19.6 | MPa | |
撕裂強(qiáng)度 | ASTM D624 | 167 | kN/m | ||
壓縮永久變形 | ASTM D395 | 62 | % | ||
懸壁梁缺口沖擊強(qiáng)度 | ASTM D256 | 無斷裂 | |||
熱性能 | 熱變形溫度 | 1.8MPa,未退火 | ASTM D648 | 117 | ℃ |
脆化溫度 | ASTM D746 | -65.0 | ℃ | ||
維卡軟化溫度 | ASTM D1525 | 193 | ℃ | ||
熔融溫度 | DSC | 216 | ℃ | ||
流動(dòng)線形膨脹系數(shù) | ASTM D696 | 0.00014 | ℃ | ||
UL 阻燃等級(jí) | UL 94 | HB | |||
電氣性能 | 體積電阻率 | ASTM D257 | 1.0E+14 | ohm.cm | |
介電強(qiáng)度 | ASTM D149 | 30 | kV/mm |