斷裂伸長率 | 520% | 拉伸強度 | 11.2MPa | 密度 | 0.918g/cm3 |
熔體流動速率 | 2.5g/10min | 維卡軟化點 | 98.9℃ | 用途級別 | 流延膜專用料,纖維 |
規(guī)格級別 | 流延膜專用料 | 加工級別 | 擠出級 |
|
產(chǎn)品簡述
斷裂伸長率 | 520% | 拉伸強度 | 11.2MPa | 密度 | 0.918g/cm3 |
熔體流動速率 | 2.5g/10min | 維卡軟化點 | 98.9℃ | 用途級別 | 流延膜專用料,纖維 |
規(guī)格級別 | 流延膜專用料 | 加工級別 | 擠出級 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||||
基本性能 | 比重 | ASTM D-792 | 0.918 | g/cm3 | ||||
熔體流動速率 | 190℃/2.16kg | ASTM D-1238 | 2.5 | g/10min | ||||
機械性能 | 電影穿刺能源 | 20.3um | Internal Method | 3.84 | J | |||
電影穿刺能源 | 50.8um | Internal Method | 8.25 | J | ||||
電影穿刺力 | 20.3um | Internal Method | 40 | N | ||||
電影穿刺力 | 50.8um | Internal Method | 84.5 | N | ||||
電影穿刺抵抗 | 20.3um | Internal Method | 26.4 | J/cm3 | ||||
電影穿刺抵抗 | 50.8um | Internal Method | 20.8 | J/cm3 | ||||
電影韌性 | 20.3um | ASTM D-882 |
|
J/cm3 | ||||
電影韌性 | 50.8um | ASTM D-882 |
|
J/cm3 | ||||
割線模量-2% Secant | 20.3um | ASTM D-882 |
|
MPa | ||||
割線模量-2% Secant | 50.8um | ASTM D-882 |
|
MPa | ||||
拉伸屈服強度 | 20.3um | ASTM D-882 |
|
MPa | ||||
拉伸屈服強度 | 50.8um | ASTM D-882 |
|
MPa | ||||
拉伸斷裂強度 | 20.3um | ASTM D-882 |
|
MPa | ||||
拉伸斷裂強度 | 50.8um | ASTM D-882 |
|
MPa | ||||
拉伸斷裂伸長率 | 20.3um | ASTM D-882 |
|
% | ||||
拉伸斷裂伸長率 | 50.8um | ASTM D-882 |
|
% | ||||
落錘沖擊 | 20.3um | ASTM D-1709A | 130 | g | ||||
落錘沖擊 | 20.3um | ASTM D-1709B | <100 | g | ||||
落錘沖擊 | 50.8um | ASTM D-1709A | 270 | g | ||||
落錘沖擊 | 50.8um | ASTM D-1709B | 170 | g | ||||
埃爾曼多夫撕裂強度 | 20.3um | ASTM D-1922 |
|
g | ||||
埃爾曼多夫撕裂強度 | 50.8um | ASTM D-1922 |
|
g | ||||
斷裂拉伸 | 0.0203mm | Internal Method | 330 | % | ||||
斷裂拉伸 | 0.0508mm | Internal Method | 520 | % | ||||
加工性能 | 熔體溫度 | 274 | ℃ | |||||
熱性能 | 維卡軟化點 | ASTM D-1525 | 98.9 | ℃ | ||||
熔化溫度 | Internal Method | 124 | ℃ | |||||
光學(xué)性能 | 光澤度 | 20°,20.3um | ASTM D-2457 | 156 | ||||
光澤度 | 20°,50.8um | ASTM D-2457 | 146 | |||||
光澤度 | 45°,20.3um | ASTM D-2457 | 95 | |||||
光澤度 | 45°,50.8um | ASTM D-2457 | 91 | |||||
霧度 | 20.3um | ASTM D-1003 | 1 | % | ||||
霧度 | 50.8um | ASTM D-1003 | 4 | ℃ |